MGO Board and EPS Connecting Adhesive

Edit: Wuxi Yalian Honeycomb Machinery Factory    Date: Dec 03, 2016
Basic Info
  • Model NO.: SPC-1003

  • Morphology: Solvent

  • Material: Polyurethane

  • Main Agent Composition: Natural Polymer

  • Promoter Composition: Curing Agent

  • Color: Yellow

  • Speed Rate: 2 - 3.5m/Min

  • Cream Time: 8~12s

  • Fire Retardant Grade: Grade Bii

  • Package2: 200kg/Iron Drum

  • Trademark: CHINAEPS

  • Origin: China

  • Bonding Function: Instant Adhesive

  • Application: Construction, Woodworking

  • Classification: Room Curing

  • Characteristic: Waterproof

  • Composition: Inorganic Material

  • Adhesive Type: Single Component System

  • Shelf Life: One Year

  • Cure Time: 48~52s

  • Package1: 25kg/Plastic Drum

  • Delivery Time: 7~15 Days After Po

  • Specification: CE

  • HS Code: 29291030

Product Description

Polyurethane glue is used for sandwich panel manufacturing, where it functions as the binding agent between nonmetallic sheet and insulation core material.

Product Features

1. Speed rate: 2 - 3.5 m/ min, can be adjusted.
2. One ton glue can cover at least 9000 square meters
3. Strong adhesion
4. Room cure
5. Applied by machine or by hand


200KG/iron drum
25 KG/plastic drum


steel sheet+rock wool
Mgo board+polystyrene
steel sheet+pearlite
steel sheet+glass fiber wool
galvanized sheet+paper honeycomb
galvanized sheet+aluminum honeycomb
color palet-EPS
color palet-XPS
calcium silicate board-EPS

Application Instruction

1. Clean the target material surface;
2. Evenly spread the adhesive, about 150g/SQM;
3. Cover the material by raising pressure (about 0.5-1.0kg/cm2).
4. Release the pressure after adhesive solidified.
5. Must press the target material within the adhesive active period, but not after the solidifyed
6. Press time: about 4 hours in summer, 6 hours in winter. 24 hours to reach the best intensity.
7. Wash the tools with acetic ether solvent.

ItemComponent A (Polyol)Component B (Isocyanate)Test Method
AppreanceYellow Brown LiquidDark Brown Viscous CreamVisual
Viscosity(Mpa.S)10001.70-2.70 poise (at 25 degree)GB/T 2794
Bonding Area90%/JC689-1996
Water(%)0.01≤0.15GB/T 12008
Acid(mgKOH/g)0.03≤3.00GB/T 12008
Hydroxyl260420-480GB/T 12008
Week odor
Boiling Point/>300 degree decomposes
Flash Point>93 degreeClosed cup: 230 degree Open cup: 230 degree
Ignition Temperature/>600 degree
Explosion Limit
Not explosive
Relative Density
1.23g/cm³ (25degree)
insoluble in water
Octanol/water Partition Coefficient
Not acceptable. Reacts with water and octanol
Vapour Density